Duasolid 50 |
 |
|||||||||||||
| 描述 | A two component oxirane ester paint containing active anti-corrosive pigments. | |||||||||||||
| 产品特性 | Used as a single coat or as a topcoat in oxirane ester based systems on steel surfaces exposed to abrasion and chemicals in severe climatic conditions. | |||||||||||||
| 推荐用途 | Suitable for earth moving machines, haulage and lifting equipment, forklifts, agricultural machinery, electric appliances, pumps and other steel structures, equipment and machinery. | |||||||||||||
| 技术参数 | ||||||||||||||
| 特性 | Excellent durability. Environmentally more friendly and for users more safe alternative than epoxy and polyurethane paints. High volume solids. High film build properties, up to 100 µm / one coat. | |||||||||||||
| 色卡 | RAL, NCS, SSG, BS, MONICOLOR NOVA and SYMPHONY colour cards. TEMASPEED tinting. Gloss varies depending on the used hardener, see application. | |||||||||||||
| 涂布率 |
Practical coverage depends on the application method, painting conditions and the shape and roughness of the surface to be coated. |
|||||||||||||
| 混合比例 | Base 2 parts by volume 527-series
Hardener 1 part by volume 008 7675 (55904), other hardeners: see apllication |
|||||||||||||
| 涂刷方法 | By airless, conventional or electrostatic spray | |||||||||||||
| 适用期 | 8 hours | |||||||||||||
| 干燥时间 |
Drying and recoating times are related to the film thickness, temperature, the relative humidity of the air and ventilation. |
|||||||||||||
| Solids volume | approx. 65 ± 2 volume %
|
|||||||||||||
| 密度 | approx. 1.5 kg / l | |||||||||||||
| 产品编号 | 527-series | |||||||||||||
| 使用说明 | ||||||||||||||
| 施工条件 | All surfaces must be dry. The temperature of the ambient air, surface or paint itself should not fall below +10 ºC during application or drying. Relative humidity should not exceed 80 %. The surface temperature of the steel should remain at least 3 ºC above the dew point. | |||||||||||||
| 准备 | Oil, grease, salts and dirt are removed by appropriate means. (ISO 12944-4)
Steel surfaces: Blast clean to grade Sa2½. (ISO 8501-1) If blast cleaning is not possible, phosphating is recommended for cold rolled steel to improve adhesion. Primed surfaces: Oil, grease, salt and dirt are removed from the surface by appropriate means. Repair any damage to the primer coat. Note the overcoating time of primer. (ISO 12944-4) |
|||||||||||||
| 涂刷底漆 | DUASOLID PRIMER and DUASOLID 50. | |||||||||||||
| 喷面漆 | DUASOLID 50. | |||||||||||||
| 涂刷 | By airless, conventional or electrostatic spray. At airless spray application the paint can be thinned if necessary to a viscosity of 20 s DIN 4. Airless spray nozzle tip "0.013 - 0.015", pressure ratio at least 30:1 and nozzle pressure 160 - 200 bar. Atomization air pressure 2 - 4 bar. At conventional spray application the viscosity should be 20 - 40 s DIN 4 and at electrostatic spraying 20 s DIN 4.
Properties and gloss of DUASOLID 50 will vary according to the used hardener: Hardener 008 7675 (55904) gloss abt. > 70 mixing ratio 2:1 Hardener 008 7670 (55953) gloss abt. >70 mixing ratio 2:1 Hardener 008 7665 (55911) gloss abt. 60 mixing ratio 2:1 Hardener 008 7667 (55917) gloss abt. 10 mixing ratio 2:1 Hardener 008 7672 (55939) gloss abt. 40 mixing ratio 2:1 Hardener 008 7666 (55907) gloss abt. > 70 mixing ratio 8:5 Hardener 008 7668 gloss abt. < 10 mixing ratio 2:1 Avoid hot spray! |
|||||||||||||
| 成分混合 | First stir base and hardener separately. The correct proportions of base and hardener must be mixed thoroughly before use. Use Temaspeed Squirrel Mixer for mixing. | |||||||||||||
| 工具清洗 | Thinner 1048 or Thinner 1112. | |||||||||||||
| EU VOC 2004/42/EC-限值 | The Volatile Organic Compounds amount is 320 g/litre of paint mixture.
VOC content of the paint mixture (thinned 15 % by volume) is 399 g/l. |
|||||||||||||