Temabond WG 300

 
Tikkurila Industry 9L
描述 A two component, low temperature curing modified epoxy paint.
产品特性 Good adhesion also to wire-brushed steel. Especially used as a primer for steel surfaces difficult to clean in process and chemical industry and in water immersion, such as ship hulls and ballast tanks. Recommended for repairing of damages caused by transport or installation and for repainting and touch-up painting of earlier painted surfaces. Can also be applied on old alkyd paint surfaces.
推荐用途 Steel surfaces.

技术参数
特性 Forms a tight coat with good chemical and abrasion resistance.
色卡 TEMASPEED tinting.
光泽组别 半光
涂布率

Recommended film thicknesses

Theoretical coverage

dry

wet

 

100 µm

145 µm

7.0 m2/l

200 µm

290 µm

3.5 m2/l


Practical coverage depends on the application method, painting conditions and the shape and roughness of the surface to be coated.
混合比例 Base 1 part by volume 176-series
Hardener 1 part by volume 008 7518
涂刷方法 By airless spray or brush.
适用期 1 hour
干燥时间

DFT 150 µm

-  5 ºC

0 ºC

+ 5 ºC

+ 10 ºC

+ 23 ºC

Dust dry, after

18 h

14 h

6½ h

3½ h

2½ h

Touch dry, after

48 h

36 h

17 h

9 h

5 h

Recoatable, after

48 h

36 h

17 h

9 h

5 h

Recoatable with epoxy,

max. without sanding

2 months

2 months

2 months

2 months

2 months

Recoatable with polyurethane, after

-

-

14 d

14 d

14 d


Drying and recoating times are related to the film thickness, temperature, the relative humidity of the air and ventilation.
Solids volume 70 ± 2 volume % (ISO 3233)
78 ± 2 weight %
密度 1.3 kg / l (mixed)
产品编号 176-series

使用说明
施工条件 All surfaces must be dry. The temperature of the ambient air and the surface should not fall below - 5 ºC during application and drying, the temperature of the paint should be at least +15 ºC. Relative humidity should not exceed 80 %. The surface temperature of the steel should remain at least 3 ºC above the dew point.
准备 Oil, grease, salts and dirt are removed by appropriate means. (ISO 12944-4)

Steel surfaces: Remove rust by tool cleaning to minimum St2 or blast clean to Sa2½ . Blast clean to grade Sa2½ for immersion. (ISO 8501-1).

Earlier painted surfaces: Roughen old paint surfaces using e.g. abrasive wheel, sand paper or blast cleaning.
涂刷底漆 TEMABOND WG 300 and TEMABOND WG 200.
喷面漆 TEMACOAT GPL, TEMACOAT GPL-S MIO, TEMACOAT GPL-S PRIMER, TEMACOAT GS 50, TEMACOAT RM 40, TEMADUR, TEMATHANE, TEMACRYL EA, TEMABOND WG 300 and TEMABOND ST 300.
涂刷 By airless spray or brush. If necessary, the paint can be thinned 0 - 10 %. Airless spray nozzle tip 0.013" - 0.019" and nozzle pressure 120 - 180 bar. Spray angle shall be chosen according to the shape of the object.
成分混合 First stir base and hardener separately. The correct proportions of base and hardener must be mixed thoroughly before use. Use Temaspeed Squirrel Mixer for mixing.
工具清洗 Thinner 1031.
EU VOC 2004/42/EC-限值 The Volatile Organic Compounds amount is 300 g/litre of paint.
VOC content of the paint mixture (thinned 10 % by volume) is 350 g/l.