Temadur SC 80

 
Tikkurila Industry 9L
描述 A two component gloss polyurethane paint, containing anticorrosive pigments, hardener aliphatic isocyanate.
产品特性 Recommended especially to be used as a single coat finish for agricultural and earth moving machinery and other machinery and equipment. Also suitable to be used as a topcoat in epoxy/polyurethane systems exposed to weathering and chemical stress
推荐用途 Storage tank exteriors, steel framework and other steel structures.

技术参数
特性 Excellent weathering and abrasion resistance. A durable, easy to clean and non-chalking topcoat with good gloss and colour retention.
色卡 RAL, NCS, SSG, BS, MONICOLOR NOVA and SYMPHONY colour cards. TEMASPEED tinting.
光泽组别
涂布率

Recommended film thicknesses/one coat application

Theoretical coverage

dry

wet

 

80 µm

125 µm

8.1 m2/l

120 µm

190 µm

5.4 m2/l

Recommended film thicknesses/as a topcoat

Theoretical coverage

dry

wet

 

40 µm

65 µm

16.2 m2/l

60 µm

95 µm

10.8 m2/l


Practical coverage depends on the application method, painting conditions and the shape and roughness of the surface to be coated.
混合比例 Base 5 parts by volume 532 series
Hardener 1 part by volume 008 7640
涂刷方法

By airless or conventional spray.

适用期 3 hours
干燥时间

DFT 60 µm

+ 5 ºC

+ 10 ºC

+ 23 ºC

+ 35 ºC

Dust dry, after

2 h

1½ h

50 min

30 min

Touch dry, after

10 h

8 h

6 h

2 h

Recoatable, after

No limitations.


Drying and recoating times are related to the film thickness, temperature, the relative humidity of the air and ventilation. When oven drying is practised in temperatures + 50 ºC - +100 ºC, the evaporation time should be 5 - 30 minutes before ovening, depending on the wet film thickness and actual temperature.
Solids volume 65 ± 2 % volume (ISO 3233)
80 ± 2 % weight
密度 1.4 ± 0.1 kg / l (mixed)
产品编号 532 series

使用说明
施工条件 All surfaces must be dry. The temperature of the ambient air, surface or paint should not fall below + 5 ºC during application or drying. Relative humidity should not exceed 80 %. The surface temperature of the steel should remain at least 3 ºC above the dew point.
准备 Oil, grease, salts and dirt are removed by appropriate means. (ISO 12944-4)

Steel surfaces: Blast clean to grade Sa2½. (ISO 8501-1) If blast cleaning is not possible, phosphating is recommended for cold rolled steel to improve adhesion.

Zinc surfaces: Sweep blast clean with mineral abrasives, e.g. quartz sand, to an even roughness. (SaS, SFS 5873) If sweep blasting is not possible, the surface should be roughened by hand abrading or washed with FONTECLEAN ZN detergent.

Hot dip galvanized surfaces are recommended to be painted with a mist coat (paint thinned 25 - 30 %) before the actual priming.

Aluminium surfaces: Sweep blast clean with non-metallic abrasives to an even roughness. (SaS, SFS 5873) If sweep blasting is not possible, the surface should be roughened by hand abrading or washed with FONTECLEAN AL detergent.

Note! Painted zinc and aluminium surfaces are not recommended when they are exposed to continuous condensation.

Primed surfaces: Oil, grease, salt and dirt are removed from the surface by appropriate means. Repair any damage to the primer coat. Note the overcoating time of primer. (ISO 12944-4)
涂刷底漆 TEMADUR PRIMER, TEMADUR 20, TEMACOAT GPL-S PRIMER, TEMACOAT GF PRIMER, TEMACOAT HB PRIMER, TEMACOAT PM PRIMER, TEMACOAT GPL-S MIO, TEMACOAT RM 40, TEMACOAT SPA MIO, TEMABOND, TEMAPRIME GF, FONTECRYL 10, FONTECRYL AP and FONTECOAT EP PRIMER.
喷面漆 TEMADUR and TEMATHANE.
涂刷 By airless or conventional spray. Airless spray: depending on the temperature of the components and shape of the object the paint can be thinned 0 - 15 %. Airless spray nozzle tip 0.011" - 0.015" and nozzle pressure 160 - 200 bar. Spray angle shall be chosen according to the shape of the object. In order to reach thicker coats (over 100 µm) use always "wet-in-wet" technique. At conventional spray the paint should be thinned 15 - 18 % to a viscosity of
20 - 25 s/DIN4.
成分混合 First stir base and hardener separately. The correct proportions of base and hardener must be mixed thoroughly before use. Use Temaspeed Squirrel Mixer for mixing.
工具清洗 Thinner 1067 or Thinner 1048.
EU VOC 2004/42/EC-限值 The Volatile Organic Compounds amount is 320 g/litre of paint.
VOC content in paint (thinned 18 % by volume) is 420 g/l.

健康安全等级
Containers are provided with safety labels, which should be observed. Further information about hazardous influences and protection are detailed in individual health and safety data sheets. A health and safety data sheet is available on request from Tikkurila Oy.
 
-