02.01.2006

Temaline BL

 
Tikkurila Industry 9L
描述 A two component, solvent free epoxy coating.
产品特性 Suitable to be used as a heavy duty coating on steel and concrete surfaces exposed to abrasion and chemical and mechanical stress in immersion.
推荐用途 Recommended for oil storage tanks, cisterns and basins in the forest industry, chemical industry and sewage purification plants etc.

技术参数
特性 Good resistance to dilute solutions of non-oxidizing acids, alkali and salts in immersion. Separate chemical resistance table available. Suitable for coating of lead-free gasoline tanks. Type approval certificate, nr. DNV 1-2-1334-1 ( Det Norske Veritas). Withstands + 150 ºC dry heat and + 60 ºC in immersion.
色彩类别 Red and green. The colour is liable to change when exposed to light or chemicals.
光泽组别
涂布率

Recommended film thicknesses

Theoretical coverage

dry

wet

 

250 µm

250 µm

4.0 m2/l

600 µm

600 µm

1.7 m2/l


Practical coverage depends on the application method, painting conditions and the shape and roughness of the surface to be coated.
混合比例 Base 3 parts by volume 008 7055-6
Hardener 1 part by volume 008 7080
涂刷方法 Dual feed hot airless spray equipment.
适用期 ½ hour
干燥时间

DFT 250 µm

+ 10 ºC

+ 23 ºC

+ 35 ºC

Dust dry, after

8 h

6 h

2 h

Touch dry, after

30 h

16 h

8 h

Recoatable without sanding, after

8 - 48 h

4 - 24 h

2 - 10 h

Fully cured, after

14 d

7 d

3 d


Drying and recoating times are related to the film thickness, temperature, the relative humidity of the air and ventilation.
Solids volume about 100 % volume (ISO 3233)
about 100 % weight
密度 1.4 kg / l (mixed)
产品编号 008 7055-6

使用说明
施工条件 All surfaces must be dry. The temperature of the ambient air, surface or paint should not fall below +10 ºC during application and drying. Relative humidity should not exceed 80 %. The surface temperature of the steel should remain at least 3 ºC above the dew point.
准备 Oil, grease, salts and dirt are removed by appropriate means. (ISO 12944-4)

Steel surfaces: Blast clean to grade Sa2½. (ISO 8501-1)

Concrete surfaces: The surface must be dry and at least 4 weeks old. The relative humidity of the concrete should not exceed 97%. Remove any splashes and unevennesses by grinding. Remove laitance and form oil from concrete castings by sanding or blast cleaning. Any cracks, crevices or voids must be repaired with a mixture of TEMALINE BL and fine dry quartz sand.
涂刷底漆 Steel surfaces: TEMALINE BL
Concrete surfaces: Impregnation with 30 % thinned TEMALINE BL
涂刷底漆 Steel surfaces: 1 x TEMALINE BL
Concrete surfaces: 2 x TEMALINE BL
涂刷 Application with a dual feed hot airless spray equipment with a pressure ratio of at least 45:1 and a theoretical litre capacity of at least 8 l/min. Optimum spray temperature is around 50 ºC at the nozzle, starting temperature about 60 ºC. Airless spray nozzle tip 0.018" - 0.027" and nozzle pressure 180 - 240 bar. Spray angle shall be chosen according to the shape of the object. Use of a reverse nozzle is recommended. Sharp edges, corners, weld seams and other areas difficult to paint should be painted by brush prior to spray application.

Note! Pot life of the mixture is about 30 min at + 23 ºC and about 5 min at + 40 ºC. Avoid to let the mixture cure in hoses, pump or spray gun.
成分混合 First stir base and hardener separately. The correct proportions of base and hardener must be mixed thoroughly before use. Use Temaspeed Squirrel Mixer for mixing.
工具清洗 Thinner 1031 or acetone.
EU VOC 2004/42/EC-限值 Does not contain Volatile Organic Compounds.
VOC content of the paint mixture (thinned 30 % by volume) is 215 g/l.

健康安全等级
Containers are provided with safety labels, which should be observed. Further information about hazardous influences and protection are detailed in individual health and safety data sheets. A health and safety data sheet is available on request from Tikkurila Oy.
 
-