Temablast EV 110

 
Tikkurila Industry 9L
描述 Two component, iron oxide pigmented epoxy shopprimer.
产品特性 Protects blast cleaned steel during storage, fabrication and construction. Does not cause any harm during welding, cutting and burning or other treating of the steel.
推荐用途 Blast cleaned steel.

技术参数
特性 The product is found to comply with: Det Norske Veritas´ Offshore Standards, Det Norske Veritas´ Rules for Classification of Ships and Det Norske Veritas´ Type Approval Programme 1-602.2, 1999, Shop Primers for Corrosion Protection of Steel Plates and Sections. The shop primer is approved for application on blast cleaned steel plates and sections. For industrial use only according to Directive 1999/13/EC.
色彩类别 Red
光泽组别 哑光
涂布率

Recommended film thicknesses

Theoretical coverage

dry

wet

 

20 µm

75 µm

13.5 m2/l


Practical coverage depends on the application method, painting conditions and the shape and roughness of the surface to be coated.
混合比例 Base 2 parts by volume 008 7920
Hardener 1 part by volume 008 7929
涂刷方法 By spray.
适用期 24 hours
干燥时间

DFT 20 µm

+ 10 ºC

+ 23 ºC

+ 35 ºC

Touch dry, after

6 min

3 - 5 min

1 min

Recoatable, after

36 h

24 h

12 h


Drying and recoating times are related to the film thickness, temperature, the relative humidity of the air and ventilation.
Solids volume 27 ± 2 % volume (ISO 3233)
48 ± 2 % weight
密度 1.2 kg / l (mixed)
产品编号 008 7920

使用说明
施工条件 All surfaces must be dry. The temperature of the ambient air, surface or paint should not fall below + 10 ºC during application or drying. Relative humidity should not exceed 80 %. The surface temperature of the steel should remain at least 3 ºC above the dew point.
准备 Oil, grease, salts and dirt are removed by appropriate means. (ISO 12944-4)

Steel surfaces: Blast clean to grade Sa2½. (ISO 8501-1) If blast cleaning is not possible, phosphating is recommended for cold rolled steel to improve adhesion.
喷面漆 Any type of paint with the exception of zinc rich paints. When selecting finishing coat for the shop primed surface, take into account the stress for which the object will be exposed. (SFS 8145)
涂刷 By spray. If necessary, the paint can be thinned 0 - 5 % to a viscosity of 16 - 18 s DIN 4/20 ºC. Airless spray nozzle tip 0.011" - 0.018" and nozzle pressure 120 - 180 bar. Spray angle shall be chosen according to the shape of the object.
成分混合 First stir base and hardener separately. The correct proportions of base and hardener must be mixed thoroughly before use. Use Temaspeed Squirrel Mixer for mixing.
工具清洗 Thinner 1031.
EU VOC 2004/42/EC-限值 The Volatile Organic Compounds amount is 610 g/litre of paint.
VOC content of the paint mixture (thinned 5 % by volume) is 625 g/l.

健康安全等级
Containers are provided with safety labels, which should be observed. Further information about hazardous influences and protection are detailed in individual health and safety data sheets. A health and safety data sheet is available on request from Tikkurila Oy.
 
-