Temaclad SC 50

产品使用说明书
-

Temaclad SC 50

描述

A two component, semigloss acrylic polyurethane with anticorrosive pigmentation. Hardener aliphatic isocyanate.

产品特性

Recommended to be used as a single coat finish for steel, aluminium and galvanized surfaces. Also suitable to be used as a topcoat in epoxy/ polyurethane systems. Not recommended for use in immersion conditions.

推荐用途

Suitable for urban, marine and industrial environments.

技术参数

特性

Outstanding colour and sheen retention. Tough, durable finish combining abrasion resistance with exceptional weathering properties, water and chemical resistance. Good cleaning properties.

色卡

RAL, NCS, SSG, BS, MONICOLOR NOVA and SYMPHONY colour cards. TEMASPEED tinting.

光泽组别

半光

涂布率

Recommended film thicknesses		Theoretical coverage
dry	wet
50 µm	90 µm	11.0 m²/l
80 µm	145 µm	6.9 m²/l

Practical coverage depends on the application method, painting conditions and the shape and roughness of the surface to be coated.

混合比例

Base 9 parts by volume 572-serie
Hardener 1 part by volume 008 7615

涂刷方法

By airless or conventional spray (large surfaces) or by brush (small surfaces).

适用期

4 hours

干燥时间

DFT 50 µm	+ 5 ºC	+ 10 ºC	+ 23 ºC	+ 35 ºC
Dust dry, after	3 h	2 h	1 h	45 min
Touch dry, after	9 h	6 h	3 h	2 h
Recoatable, min., after	30 h	24 h	12 h	8 h

Drying and recoating times are related to the film thickness, temperature, the relative humidity of the air and ventilation.

Solids volume

55 ± 2 % volume (ISO 3233)
69 ± 2 % weight

密度

1.3 ± 0.1 kg / l (mixed)

产品编号

572-serie

使用说明

施工条件

All surfaces must be dry. The temperature of the substrate should be above 0 °C and at least 3 ° above the dew point of the air. The temperature of the paint has to be over + 15 °C. If the temperature of the substrate is over + 50 °C, painting is not recommended. Good ventilation is required in confined areas to ensure proper drying. Condensation occurring during or immediately after application may result in matt finish and an inferior film.

准备

Primed surfaces: Oil, grease, salt and dirt are removed from the surface by appropriate means. (SFS-ISO 12944-4)

Steel surfaces: Blast clean to grade Sa2½. (SFSISO 8501-1) If blast cleaning is not possible, phosphating is recommended for cold rolled steel to improve adhesion.

Zinc surfaces: Sweep blast clean with mineral abrasives, e.g. quartz sand, to an even roughness. (SaS, SFS 5873) If sweep blasting is not possible, the surface should be roughened by hand abrading or washed with FONTECLEAN ZN detergent.

Aluminium surfaces: Sweep blast clean with non-metallic abrasives to an even roughness. (SaS, SFS 5873) If sweep blasting is not possible, the surface should be roughened by hand abrading or washed with FONTECLEAN AL detergent.

Primed surfaces: Oil, grease, salt and dirt are removed from the surface by appropriate means. Repair any damage to the primer coat. Note the overcoating time of primer. (SFS-EN ISO 12944-4)

Old alkyd and coil- coated ( not PVDF) surfaces: Remove rust and white rust by power tool cleaning to St 2. Hard, glossy paint surfaces should be roughened by abrading. Oil, grease, salt ,dirt and dust are removed by washing with FONTECLEAN ZN detergent.

涂刷底漆

TEMAPRIME EE and TEMACOAT GF. Suitable to be used without primer.

喷面漆

TEMACLAD SC 50.

涂刷

By airless or conventional spray (large surfaces) or by brush (small surfaces). In order to obtain an even, non-porous finish, spray a misty coat: first a thin layer, then let the solvents evaporate for 5 - 30 minutes and then apply the full coat. Depending on the application method and the temperature of the components (base, hardener, thinner) the paint can be thinned 0 - 10 %. Airless spray nozzle tip 0.011" - 0.015"; pressure 120 - 160 bar, spray angle shall be chosen according to the shape of the object. At brush application the paint should be thinned according to the circumstancies.

成分混合

First stir base and hardener separately. The correct proportions of base and hardener must be mixed thoroughly before use. Use a mechanical agitator for mixing. Insufficient mixing or incorrect ratio will result in uneven drying and weaken the properties .

工具清洗

Thinner 1048 or 1067.

EU VOC 2004/42/EC-限值

The Volatile Organic Compounds amount is 420 g/litre of paint mixture.
VOC content of the paint mixture (thinned 10% by volume) is 460g/l.

健康安全等级

Containers are provided with safety labels, which should be observed. Further information about hazardous influences and protection are detailed in individual health and safety data sheets. A health and safety data sheet is available on request from Tikkurila Oy.

上述信息，基于实验室测试和实际应用而获得，产品使用说明书记载了其被验证有效的日期，我们的生产体系通过了ISO9001和ISO14001认证，可充分保证该产品的质量。对不按使用说明施工和产品用于不当场合所带来的任何损失，作为生产商，我们不会承担任何责任。