Temacoat GPL-S MIO

产品使用说明书
12.02.2008

Temacoat GPL-S MIO

描述

A two component, polyamide cured epoxy paint pigmented with micaceous iron oxide.

产品特性

Used as an intermediate or finishing coat in epoxy and polyurethane systems exposed to severe weathering and splashes.

推荐用途

Recommended for bridges, exteriors of tanks, steel frameworks, conveyors, tubular bridges and other steel structures and equipment.

技术参数

特性

Forms a very strong and durable coat due to the micaceous iron oxide pigment. Rapidly recoatable. Can be overcoated after prolonged period.

色彩类别

Grey.

光泽组别

哑光

涂布率

Recommended film thicknesses		Theoretical coverage
dry	wet
60 µm	100 µm	10.0 m²/l
125 µm	210 µm	4.8 m²/l

Practical coverage depends on the application method, painting conditions and the shape and roughness of the surface to be coated.

混合比例

Base 4 parts by volume 008 7520
Hardener 1 part by volume 008 5600 or 008 5605 (fast)

涂刷方法

By airless spray or brush.

适用期

6 hours with Hardener 008 5600
3 hours with Hardener 008 5605

干燥时间

DFT 80 µm		0 ºC	+ 5 ºC	+ 10 ºC	+ 23 ºC	+ 35 ºC
Dust dry, after	with Hardener 008 5600	4 h	2 h	1 h	½ h	15 min
Dust dry, after	with Hardener 008 5605	3 h	1½ h	¾ h	½ h	12 min
Touch dry, after	with Hardener 008 5600	22 h	12 h	6 h	2½ h	1 ½ h
Touch dry, after	with Hardener 008 5605	12 h	6 h	4 h	2 h	1 h
Recoatable with epoxy paints, min. after	with Hardener 008 5600	30 h	20 h	6 h	2 h	1 h
Recoatable with epoxy paints, min. after	with Hardener 008 5605	18 h	12 h	4 h	1½ h	¾ h
Recoatable with polyurethane paints, min. after	with Hardener 008 5600	2 d	32 h	18 h	8 h	5 h
Recoatable with polyurethane paints, min. after	with Hardener 008 5605	1 ½ d	18 h	12 h	5 h	3 h

Drying and recoating times are related to the film thickness, temperature, the relative humidity of the air and ventilation.

Solids volume

60 ± 2 % volume (ISO 3233)
78 ± 2 % weight

密度

1.5 kg / l (mixed)

产品编号

008 7520

使用说明

施工条件

All surfaces must be clean and dry and free from contamination. The temperature of the substrate should be minimum 0 °C and at least 3 ° C above the dew point of the air. The product should not be applied at temperatures below 0 °C where there is a possibility of ice formation on the substrate. The temperature of paint itself should be above + 15 °C for proper application. Good ventilation is required in confined areas during application and drying.

Note! There is a natural tendency of epoxy coatings to chalk and discolor on exterior exposure

准备

Primed surfaces: Oil, grease, salt and dirt are removed from the surface by appropriate means. Repair any damage to the primer coat. Note the overcoating time of primer. (ISO 12944-4)

涂刷底漆

TEMAZINC 77, TEMAZINC 88, TEMAZINC 99, TEMACOAT GPL-S PRIMER, TEMASIL 90 and TEMABOND.

喷面漆

TEMACOAT GPL, TEMACOAT GS 50, TEMACOAT RM 40, TEMADUR 20, TEMADUR 50, TEMADUR 90, TEMADUR HB 50, TEMADUR HB 80, TEMATHANE 50 and TEMATHANE 90.

涂刷

By airless spray or brush. At spray application the paint should be thinned 0 - 10 %. Airless spray nozzle tip 0.015" - 0.021" and nozzle pressure 120 - 180 bar. Spray angle shall be chosen according to the shape of the object. At brush application the paint should be thinned according to the circumstancies.

成分混合

First stir base and hardener separately. The correct proportions of base and hardener must be mixed thoroughly before use. Use Temaspeed Squirrel Mixer for mixing.

工具清洗

Thinner 1031.

EU VOC 2004/42/EC-限值

The Volatile Organic Compounds amount is 340 g/litre of paint.
VOC content of paint mixture (thinned 10 % by volume) is 400 g/l.

健康安全等级

Containers are provided with safety labels, which should be observed. Further information about hazardous influences and protection are detailed in individual health and safety data sheets. A health and safety data sheet is available on request from Tikkurila Oy.

上述信息，基于实验室测试和实际应用而获得，产品使用说明书记载了其被验证有效的日期，我们的生产体系通过了ISO9001和ISO14001认证，可充分保证该产品的质量。对不按使用说明施工和产品用于不当场合所带来的任何损失，作为生产商，我们不会承担任何责任。