Temaprime GF

Tikkurila Industry 9L
描述 A fast drying, one component anti-corrosive pigmented special primer.
产品特性 Primer for steel, aluminium and zinc surfaces. Recoatable also with polyurethane paints. Can also be used without any topcoat for steel surfaces in dry indoor areas.
推荐用途 Recommended uses e.g. haulage equipment, agricultural, construction and other machinery.

特性 Excellent anti-corrosive properties.
色彩类别 Grey (TVT 4001.) TEMASPEED tinting.
光泽组别 哑光

Recommended film thicknesses

Theoretical coverage




40 µm

80 µm

12.5 m2/l

60 µm

120 µm

8.3 m2/l

Practical coverage depends on the application method, painting conditions and the shape and roughness of the surface to be coated.
涂刷方法 By airless spray or by brush.

DFT 50 µm

+ 10 ºC

+ 23 ºC

+ 35 ºC

Dust dry, after

50 min

15 min

10 min

Touch dry, after

2 h

1 h

30 min

Recoatable, min. after

2 h

1 h

30 min

Drying and recoating times are related to the film thickness, temperature, the relative humidity of the air and ventilation.
Solids volume 50 ± 2 % volume (ISO 3233)
68 ± 2 % weight
密度 1.3 kg / l
产品编号 187-series

施工条件 All surfaces must be dry. The temperature of the ambient air, surface or paint should not fall below 5 ºC during application and drying. The relative humidity should not exceed 80 %. The temperature of the substrate should remain at least 3 ºC above the dew point.
准备 Oil, grease, salts and dirt are removed by appropriate means. (ISO 12944-4)

Steel surfaces: Blast clean to grade Sa2½. (ISO 8501-1) If blast cleaning is not possible, phosphating is recommended for cold rolled steel to improve adhesion.

Zinc surfaces: Sweep blast clean with mineral abrasives, e.g. quartz sand, to an even roughness. (SaS, SFS 5873) If sweep blasting is not possible, the surface should be roughened by hand abrading or washed with FONTECLEAN ZN detergent.

Hot dip galvanized surfaces are recommended to be painted with a mist coat (paint thinned 25 - 30 %) before the actual priming.

Aluminium surfaces: Sweep blast clean with non-metallic abrasives to an even roughness. (SaS, SFS 5873) If sweep blasting is not possible, the surface should be roughened by hand abrading or washed with FONTECLEAN AL detergent.

Primed surfaces: Oil, grease, salt and dirt are removed from the surface by appropriate means. Repair any damage to the primer coat. Note the overcoating time of primer. (ISO 12944-4)
涂刷 By airless spray or by brush. Mix the paint thoroughly before use. The paint can be thinned 0 - 15 % at airless spray application. Airless spray nozzle tip 0.011" - 0.013" and nozzle pressure 120 - 180 bar. Spray angle shall be chosen according to the shape of the object. Large surfaces Thinner 1053 (slow).
工具清洗 Thinner 1006.
EU VOC 2004/42/EC-限值 The Volatile Organic Compounds amount to 440 g/litre of paint.
VOC content of the paint (thinned 30 % by volume) is 546 g/l.

Containers are provided with safety labels, which should be observed. Further information about hazardous influences and protection are detailed in individual health and safety data sheets. A health and safety data sheet is available on request from Tikkurila Oy.