Temazinc 99

 
Tikkurila Industry 9L
描述 A two component, polyamide cured zinc rich epoxy paint.
产品特性 Used as a primer in epoxy, polyurethane, acrylic and chlorinated rubber systems for steel surfaces exposed to severe climatic conditions. Can be used without a topcoat on surfaces exposed to weathering.
推荐用途 Recommended for bridges, cranes and steel frameworks as well as steelwork and equipment in the forest and chemical industries, such as tubular bridges, conveyors etc.

技术参数
特性 Offers cathodic protection for steel.
色彩类别 Grey.
光泽组别 哑光
涂布率

Recommended film thicknesses

Theoretical coverage

dry

wet

 

40 µm

70 µm

13,8 m2/l

80 µm

145 µm

6.9 m2/l


Practical coverage depends on the application method, painting conditions and the shape and roughness of the surface to be coated.
混合比例 Base 3 parts by volume 008 7400
Hardener 1 part by volume 008 7440
涂刷方法 By airless spray or brush.
适用期 30 hours
干燥时间

DFT 40 µm

+ 5 ºC

+ 10 ºC

+ 23 ºC

+ 35 ºC

Dust dry, after

50 min

20 min

10 min

5 min

Touch dry, after

2 h

1 h

30 min

15 min

Recoatable, min. after

5 h

3 h

1 h

30 min


Drying and recoating times are related to the film thickness, temperature, the relative humidity of the air and ventilation.
Solids volume 55 ± 2 % volume (ISO 3233)
密度 2.6 kg / l (mixed)
产品编号 008 7400

使用说明
施工条件 All surfaces must be dry. The temperature of the ambient air, surface or paint should not fall below +5 ºC during application and drying. Relative humidity should not exceed 80 %. The surface temperature of the steel should remain at least 3 ºC above the dew point.
准备 Oil, grease, salts and dirt are removed by appropriate means. (ISO 12944-4)

Steel surfaces: Blast clean to grade Sa2½. (ISO 8501-1)
喷面漆 TEMACOAT GPL-S PRIMER, TEMACOAT GF PRIMER, TEMACOAT HB PRIMER, TEMACOAT GPL-S MIO, TEMACOAT GS 50, TEMACOAT RM 40, TEMACOAT HB 30, TEMACOAT SPA, TEMABOND, TEMACHLOR 40, TEMACRYL AR 50 and TEMANYL MS PRIMER.
涂刷 By airless spray or brush. Agitate during application. Depending on the application method the paint can be thinned 0 - 10 % by volume. Airless spray nozzle tip 0.015" - 0.021" and nozzle pressure 120 - 180 bar. Spray angle shall be chosen according to the shape of the object. Sharp edges, corners, weld seams and other areas difficult to cover properly by spray application should be coated by brush before the spray application. At brush application the paint should be thinned according to the circumstancies.
成分混合 First stir base and hardener separately. The correct proportions of base and hardener must be mixed thoroughly before use. Use Temaspeed Squirrel Mixer for mixing.
工具清洗 Thinner 1031.
EU VOC 2004/42/EC-限值 The Volatile Organic Compounds amount is 430 g/litre of paint.
VOC content of the paint mixture (thinned 10 % by volume) is 473 g/l.