Fontecryl AP
|
|
描述 |
A waterborne, one component fast drying acrylic based primer containing active anticorrosive pigments. |
产品特性 |
Recommended to be used as an anti-corrosive primer on steel, aluminium and zinc surfaces. Suitable also for dipping. Drying times can be shortened by using higher temperatures. Overcoatable with a wide range of products, also with solventborne products. |
推荐用途 |
Steel, aluminium and zinc surfaces. |
|
技术参数 |
色彩类别 |
Black, grey, yellow, iron oxide red, green, dark grey, RAL 8017 and TEMASPEED FONTE tinting.. |
光泽组别 |
哑光 |
涂布率 |
Recommended film thicknesses |
Theoretical coverage |
dry |
wet |
|
40 µm |
125 µm |
8.3 m2/l |
Recommended film thicknesses with Duasolid 50 as a topcoat |
Theoretical coverage |
dry |
wet |
|
20 µm |
60 µm |
16.5 m2/l | Practical coverage depends on the application method, painting conditions and the shape and roughness of the surface to be coated.
|
稀释剂 |
水 |
涂刷方法 |
By spray or dip. |
干燥时间 |
DFT 40 µm |
+ 15 ºC |
+ 23 ºC |
+ 60 ºC |
Dust dry, after |
2 h |
30 min |
5 min |
Touch dry, after |
2 ½ h |
1 h |
15 min |
Recoatable , min. after |
24 h |
1 - 2 h |
30 min | Drying and recoating times are related to the film thickness, temperature, the relative humidity of the air and ventilation.
|
Solids volume |
33 ± 2 % volume |
密度 |
1.2 kg / l |
产品编号 |
006 5970, -71, -72, -73, -74, -75, -76, 539-series |
|
使用说明 |
施工条件 |
All surfaces must be dry. The temperature of the ambient air, surface or paint should not fall below +15 ºC during application or drying. Relative humidity should be between 20 - 70 %. The surface temperature of the steel should remain at least 3 ºC above the dew point. |
准备 |
Oil, grease, salts and dirt are removed by appropriate means. (ISO 12944-4)
Steel surfaces: Blast clean to grade Sa2½. (ISO 8501-1) If blast cleaning is not possible, phosphating is recommended for cold rolled steel to improve adhesion. |
涂刷底漆 |
FONTECRYL AP. |
喷面漆 |
DUASOLID 50, TEMADUR SC, FONTELAC QD 80 and FONTECRYL 50. |
涂刷 |
By spray or dip. Depending on the application method the paint can be thinned 0 - 15 %. At dip application the viscosity should be 20 - 25 s DIN 4.
Note! The viscosity falls quickly when thinning the paint. |
工具清洗 |
FONTECLEAN 1921. |
EU VOC 2004/42/EC-限值 |
The Volatile Organic Compounds amount is 120 g/litre of paint.
VOC content in paint (thinned 15 % by volume) is 100 g/l. |
|
健康安全等级 |
|
Containers are provided with safety labels, which should be observed. Further information about hazardous influences and protection are detailed in individual health and safety data sheets.
A health and safety data sheet is available on request from Tikkurila Oy. |
|
- |
|