Akrodur 90

Tikkurila Industry 9L
描述 A two component polyurethane lacquer.
产品特性 Recommended for wooden and synthetic material surfaces.
推荐用途 -

特性 Forms a very tight, tough coat with good resistance to abrasion and weather. Excellent resistance to chemicals.
光泽组别 全光
排放等级 The lacquer does not contain free formaldehyde and after drying it does not emit formaldehyde to the environment.

3 - 5 m2/l (100 μm).

Practical coverage depends on the application method, painting conditions and the shape and roughness of the surface to be coated.
稀释剂 ,
混合比例 Lacquer 100 parts by volume 007 1180
Hardener 15 parts by volume 007 1210 or 30 parts by volume 990 0928

Application technique

Viscosity DIN4

Low pressure

18 - 25 s

Airless spraying

20 - 25 s

Curtain coating

35 - 45 s

适用期 8 hours

(110 - 120 g/m2)

50 ºC

70 ºC

Dry to handle, after

1 h

40 - 50 min

Stacking temperature below 35 ºC.


Drying and recoating times are related to the film thickness, temperature, the relative humidity of the air and ventilation.
Solids volume abt. 37 % by volume, 43 % by weight
密度 0.97 kg/litre
产品编号 007 1180

施工条件 The surface to be treated has to be clean and dry. During application and drying the temperature of the air, the surface to be treated and the lacquer has to be over 18 ºC and the relative humidity of the air below 70 %.
喷面漆清漆 Stir the lacquer well. Add 15 % by volume Hardener 007 1210 and mix well again. Thin the lacquer to the desired viscosity using Thinner 1062, 1082 or 1048.
工具清洗 Thinner 1082.
EU VOC 2004/42/EC-限值 The Volatile Organic Compounds amount to 550 ± 20 g/l.

Containers are provided with safety labels, which should be observed. Further information about hazardous influences and protection are detailed in individual health and safety data sheets. A health and safety data sheet is available on request from Tikkurila Oy. For professional use only.