产品使用说明书 13.01.2006 |
|||||||||||
Merit Combi 25 |
 |
|||||||||||
| 描述 | A one component acid catalysed lacquer. | |||||||||||
| 产品特性 | A fast drying, easy to sand priming and finishing lacquer without aromatic solvents. | |||||||||||
| 推荐用途 | Recommended for furniture, doors and other similar wooden surfaces. | |||||||||||
| 技术参数 | ||||||||||||
| 光泽组别 | 半哑光 | |||||||||||
| 排放等级 | Fulfils the requirements of DIN-norm 55 666, formaldehyde content max. 0.12 mg/m3 air. | |||||||||||
| 涂布率 |
Practical coverage depends on the application method, painting conditions and the shape and roughness of the surface to be coated. |
|||||||||||
| 涂刷方法 |
|
|||||||||||
| 干燥时间 |
Stacking temperature below 35 ºC. Drying and recoating times are related to the film thickness, temperature, the relative humidity of the air and ventilation. |
|||||||||||
| Solids volume | abt. 26 volume-%, 34 weight-%. | |||||||||||
| 密度 | 0.9 kg/litre | |||||||||||
| 储存 | 6 months | |||||||||||
| 产品编号 | 005 2758 | |||||||||||
| 使用说明 | ||||||||||||
| 施工条件 | The surface to be treated has to be clean and dry. During application and drying the temperature of the air, the surface to be treated and the lacquer has to be over 18 ºC and the relative humidity of the air below 70 %. | |||||||||||
| 喷面漆清漆 | Stir the lacquer carefully before use. Thin to the viscosity required with Thinner 1035 or 1033. Do not use iron containers as mixing container. Instead use plastic, enamel or acid resistant steel containers. | |||||||||||
| 工具清洗 | Thinner 1035 or 1033. | |||||||||||
| EU VOC 2004/42/EC-限值 | The Volatile Organic Compounds amount is 610 g/litre of paint.
Maximum VOC content in ready to use paint (thinned 20 % by volume) is 642 g/l. |
|||||||||||
| 健康安全等级 | ||||||||||||
| Containers are provided with safety labels, which should be observed. Further information about hazardous influences and protection are detailed in individual health and safety data sheets. A health and safety data sheet is available on request from Tikkurila Oy. | ||||||||||||
| - | ||||||||||||